1.2343 / X37CRMOV5-1 ASLOVCHI POʻlat SHAKLI, Oʻlchami va taʼminotga chidamliligi
| ta'minot shakli | Hajmi (mm) | Jarayon | Tolerantlik | |
Dumaloq | P6-PH100 | sovuq chizish | Yaltiroq / Qora | eng yaxshi h11 |
| PH16-PH350 | issiq haddelenmiş | Qora | -0 / ortiqcha 1 mm | |
| tozalangan / maydalangan | eng yaxshi h11 | |||
| P90-P1000 | issiq soxta | Qora | -0 / ortiqcha 5 mm | |
| qo'pol | -0 / ortiqcha 3 mm | |||
| Yassi / kvadrat / blok | Qalinligi: 120-800 | issiq soxta | Qora | -0 / ortiqcha 8 mm |
| Kengligi: 120-1500 | qo'pol ishlov berish | -0 / ortiqcha 3 mm |
Izoh: Tolerantlik so'rovlar bo'yicha sozlanishi mumkin
1.2343/X37CRMOV5-1 ASLOVCHILIK POʻLOTI KIMYOVIY TARKIBI
| MALAKA | NUMBER | C | Va shunday | Minnesota | P | Va shunday | Cr | oy | v |
| X37CrMoV5-1 | 0.33-0.41 | 0.80-1.20 | 0.25-0.50 | 0.030 dan kichik yoki unga teng | 0.020 dan kichik yoki unga teng | 4.80-5.50 | 1.10-1.50 | 0.30-0.50 | |
| 1.2343 | 0.36-0.42 | 0.90-1.20 | 0.30-0.50 | 0.030 dan kichik yoki unga teng | 0.030 dan kichik yoki unga teng | 4.80-5.50 | 1.10-1.40 | 0.25-0.50 |
1.2343/X37CRMOV5-1 TO'P PO'lat Jismoniy Xususiyati
| Harorat | 20 daraja S | 200 daraja S | 400 daraja S | 600 daraja S |
| Zichlik, kg/m3 | 7800 | 7750 | 7700 | 7600 |
| Elastiklik moduli, Mpa | 210000 | 200000 | 180000 | 140000 |
| Issiqlik kengayish koeffitsienti 20 darajadan , daraja uchun | - | 11,6×10^-6 | 12,4×10^-6 | 13,2×10^-6 |
| Issiqlik o'tkazuvchanligi, Vt / m darajasi | - | 30 | 30 | 31 |
1.2343/X37CRMOV5-1 ASLOVCHI POʻLODINI MEXANIK XUSUSIYATLARI
| Qattiqlik, HRC | To'rt. Besh | 46.5 | 48.5 |
| Kuchlanish kuchi, Mpa | 1450 | 1580 | 1680 |
| Hosildorlik kuchi Rp 0.2, Mpa | 1240 | 1340 | 1410 |
| Uzayish A5, foiz | 13 | 13 | 12 |
| Z maydonining qisqarishi, foiz | 65 | 65 | 64 |
1.2343/X37CRMOV5-1 QUVVATLASH UCHUN PO'lat
1.2343/X37CrMoV5-1 asbob poʻlatlari 900-1120 darajada zarb qilinadi. Harorat 900 darajadan past bo'lganda qayta isitish kerak, 1,2343/X37CrMoV5-1 asbob po'latlari o'choqda iloji boricha sekin sovutilishi kerak; zarbdan keyin tavlanish tavsiya etiladi.
1.2343 / X37CRMOV5-1 Stressni Yengillashtiruvchi asbob
Ishlov berish kuchlanishlarini olib tashlash uchun stressni bartaraf qilish 650 darajaga qadar qizdirish, bir soat davomida issiq ushlab turish, pechda sovutish orqali amalga oshirilishi kerak. Bu operatsiya issiqlik bilan ishlov berish paytida buzilishlarni kamaytirish uchun amalga oshiriladi.
1.2343 / X37CRMOV5-1 TAVLANILGAN ASLOVCHI PO'lat
Sekin va teng ravishda 845 ~ 900 gradusgacha qizdiring, pechni soatiga 10 ~ 20 daraja tezlikda 540 darajaga sovutib, HB 229 qattiqligini oling.
1.2343 / X37CRMOV5-1 PO'LATNI QATTISH
1000-1040 daraja haroratda qattiqlashish, keyin havo bilan o'chirish, yog'ni o'chirish yoki issiq suvda sovutish 500-550 daraja
C. Söndürmeden keyingi qattiqlik 50-56 HRC.
1.2343 / X37CRMOV5-1 QATTIQLANGAN ALBATTA PO'lat
54 dan 38 gacha bo'lgan Rockwell C qattiqligi uchun 540 dan 650 gradusgacha qizdiring. Xona haroratiga oraliq sovutish bilan kamida ikki marta haroratni oshiring. Haroratda saqlash muddati kamida 2 soat.
| Jahldor, daraja | 100 | 200 | 300 | 400 | 500 | 550 | 600 | 650 | 700 |
| HRC | 53 | 52 | 52 | 52 | 54 | 52 | 48 | 38 | 30 |
| Rm, N/mm2 | 1845 | 1790 | 1790 | 1790 | 1910 | 1790 | 1570 | 1200 | 970 |
1.2343/X37CRMOV5-1 ALBATTA PO'LIT QO'LLANISHI
Asbob po'lati 1.2343 / X37CrMoV5-1 yuqori kuchlanishli issiq ish asboblari uchun keng qo'llaniladi, odatiy foydalanish:
1.Ekstruziya sanoati: ekstruziya qoliplari va konteynerlari
2.Forging sanoati: qolib shakllantirish, press qoliplari 3.Die
-quyma sanoati: karbid uchun o'lik
4. Samolyot sanoati: qo'nish moslamalari, ushlab turuvchi ilgaklar
Issiq teglar: 1.2343 / x37crmov5-1 asbob po'lati, yetkazib beruvchi, moslashtirilgan, ulgurji, arzon, chegirma, narxlar ro'yxati, arzon narx, stokda, bepul namuna