| Standart | Daraja | ||||||
|---|---|---|---|---|---|---|---|
| Kimyoviy tarkibi | |||||||
| C: | Ha: | Mn: | Savol: | S: | Cr: | Ikkalasi ham: | Siz: |
| PN | 18HGT | ||||||
| 0,17-0,23 | 0,17-0,37 | 0,8-1,1 | <0.035 | <0.035 | 1,0-1,3 | <0.3 | 0,05-0,12 |
| GOST | 18ChGT | ||||||
| 0,17-0,23 | 0,17-0,37 | 0,8-1,1 | <0.035 | <0.035 | 1,0-1,3 | <0.3 | 0,03-0,09 |
| GOST | 18ChGT-Sh | ||||||
| 0,17-0,23 | 0,17-0,37 | 0,8-1,1 | <0.025 | <0.015 | 1,0-1,3 | <0.3 | 0,03-0,09 |
| ČSN | 14223 | ||||||
| 0,17-0,23 | 0,17-0,37 | 0,8-1,1 | <0.035 | <0.035 | 1,0-1,3 | - | 0,04-0,10 |
| STAS | 21TiMnCr12 | ||||||
| 0,17-0,23 | 0,17-0,37 | 0,8-1,1 | <0.035 | <0.035 | 1,0-1,3 | <0.3 | 0,03-0,09 |
18HGT, 18ChGT, 21TiMnCr12, 14223 - tavsifi
Po'lat tishli va vites qutisi vallari kabi yuqori yadro kuchini talab qiladigan yuqori yuklangan strukturaviy qismlar uchun ishlatiladi. U haddan tashqari qizib ketishga katta qarshilik ko'rsatadi va yuqori haroratlarda tezda karbüratsiyalanadi. Payvandlanadigan, ishlov beriladigan va kesiladigan po'lat. U karbürizatsiyadan oldin va keyin payvandlanishi mumkin.
Fizikaviy va mexanik xususiyatlar
Ta'sir KCU, 20 daraja:
| Mexanik xususiyatlar | Standart/darajali | ||||
|---|---|---|---|---|---|
| PN | GOST | ČSN | STAS | ||
| 18HGT | 18ChGT | 14223 | 21TiMnCr12 | ||
| Payvandlash kuchi: | RM | >830 MPa | >885 MPa | >740 MPa | >880 MPa |
| Mustahkamlik chegarasi: | RM | >980 MPa | >980 MPa | 880-1180MPa | 1180-150MPa |
| Cho'zilish: | A5 | 9% | 9% | 10% | 9% |
| KCU2 J/sm2 | 80 J/sm2 | 79 J/sm2 | 69 J/sm2 | - | |
| Tavlanish holatidagi qattiqlik | H.B. | 217 H.B. | 217 H.B. | 197 H.B. | 217 H.B. |
Qattiqlashgandan keyin mexanik xususiyatlar:
Diametri D: 11 mm
Kuchlanish kuchi Rm: 920-1270 MPa
Chiqish qarshiligi Re: min 600 MPa
Cho'zilish A: min. 9 %.
KU ta'sir qiymati: min 25 J
Diametri D: 30 mm
Kuchlanish kuchi Rm: 820-1170 MPa
Kuchlanish kuchi Re: min 540 MPa
Cho'zilish A: min. 10 %.
KU ta'sir qiymati: min 25 J
Diametri D: 63 mm
Kuchlanish quvvati Rm: 710-1060 MPa
Kuchlanish kuchi Re: min 480 MPa
Cho'zilish A: min. 11 %.
KU ta'sir qiymati: min 25 J
| Davolash | Daraja | ||||
|---|---|---|---|---|---|
| PN | GOST | ČSN | STAS | ||
| 18HGT | 18ChGT | 14223 | 21TiMnCr12 | ||
| Jahldor | Harorat | 810-830 daraja | 880-950 daraja | 850-880 daraja | 875-910 daraja |
| Sovutish | moy | havo | moy | moy | |
| Jahldor | Harorat | 200 daraja | 200 daraja | 150-200 daraja | 170-190 daraja |
| Sovutish | havo, moy | pech, moy | havo, moy | havo, moy | |
Termik va termokimyoviy ishlov berishning boshqa texnologik jarayonlarining haroratlari:
Karbonitridlanish: 860-930 daraja
Qattiqlashuv va karburizatsiya: 850-880 daraja. Suvda yoki yog'da sovutish. Karbürizatsiyadan keyin tavlanish: 660-680 daraja Karbürizatsiyadan keyin qattiqlashish II: 810-830 daraja. Suvda yoki yog'da sovutish. Karbürizing temperleme: 150-200 daraja.
Biz ushbu po'lat qotishmasini quyidagicha etkazib beramiz:
Rodlar, chiziqlar va g'altaklar Rod